| 廠家(產(chǎn)地) | 美國杜邦 | 牌號 | 100p |
| 類型 | 標準料 | 規(guī)格級別 | 注塑 增韌 |
| 拉伸強度 | 69 | 密度 | 1.42 |
| 缺口沖擊強度 | 137 | 彎曲模量 | 2840 |
| 彎曲強度 | 98 | 用途 | 高應力零件，加工素材、板、條、管。 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 吸水量 | 50%相對濕度 | ASTM D-570 | 0.22 | % |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.25 | % |
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.90 | % |
| 比重 | ASTM D-792 | 1.42 | ||
| 自燃性 | UL 94 | HB | ||
| IZOD沖擊試驗 | 無缺口23℃ | ASTM D-256 | >5300 | j/m |
| 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >260 | % |
| 洛氏硬度 | ASTM D-785 | 94 | M scale | |
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1580 | MPa |
| 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 14.9 | 10-5m/m℃ |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 40 | % |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 98 | MPa |
| 負載變形量 | 140kg/cm250℃ | ASTM D-621 | 0.5 | % |
| 撓曲疲勞忍耐限度 | 50%RH 23℃ 106周期 | ASTM D-671 | 32 | MPa |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 2840 | MPa |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 685 | MPa |
| 抗剪強度 | 23℃ | ASTM D-732 | 66 | MPa |
| IZOD沖擊試驗 | 23℃ | ASTM D-256 | 137 | j/m |
| 拉伸強度 | 70℃ | ASTM D-638 | 48 | MPa |
| 壓縮應力 | 23℃ 10%變形 | ASTM D-695 | 123 | MPa |
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 65 | % |
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 4120 | MPa |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 3220 | MPa |
| IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 98 | j/m |
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 525 | kj/m2 |
| 模收縮 | 2.2-2.4 | % | ||
| 洛氏硬度 | ASTM D-785 | 120 | R scale | |
| 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm |
| 拉伸強度 | 122℃ | ASTM D-638 | 26 | MPa |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 1030 | MPa |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >260 | % |
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 172 | ℃ |
| 拉伸強度 | -55℃ | ASTM D-638 | 101 | MPa |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | 230 | % |
| 壓縮應力 | 23℃ 1%變形 | ASTM D-695 | 35 | MPa |
| 拉伸強度 | 100℃ | ASTM D-638 | 36 | MPa |
| 拉伸強度 | 23℃ | ASTM D-638 | 69 | MPa |
| 抗電弧 | 3.1mm | ASTM D-495 | 220 | sec |
| 介電因數(shù) | 50%RH 23℃ 106Hz | ASTM D-150 | 0.005 | |
| 容積電阻率 | 23℃ 0.2%含水量 | ASTM D-257 | 1×1015 | Ω.cm |
| 介電常數(shù) | 50%RH 23℃ 102～106Hz | ASTM D-150 | 3.7 | Ω.cm |
| 熱傳導系數(shù) | 0.37 | W/mk | ||
| 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 10.4 | 10-5m/m℃ |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 136 | ℃ |
| 線性熱膨脹系數(shù) | 29～60℃ | ASTM D-696 | 12.2 | 10-5m/m℃ |
| 熔點 | ASTM D-2133 | 175 | ℃ | |
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 13.7 | 10-5m/m℃ |