美國液氮PPS Lubricomp OFL-4036 產(chǎn)品特性：OFL36，含30%玻璃纖維和聚四氟乙烯，耐熱，潤滑好，機(jī)械強(qiáng)度高，電性能好，阻燃自熄，線性高分子結(jié)構(gòu)
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費(fèi)提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
PPS OFL-4036 物性數(shù)據(jù)：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.10 to 0.20 | % | ASTM D955 |
| Molding Shrinkage - Across Flow (24 hr) | 0.60 to 0.80 | % | ASTM D955 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow: 24 hr | 0.30 to 0.48 | % | |
| Flow: 24 hr | 0.13 to 0.18 | % | |
| Water Absorption (24 hr, 50% RH) | 0.0012 | % | ASTM D570 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 2 | 12800 | MPa | ASTM D638 |
| Tensile Modulus | 12000 | MPa | ISO 527-2/1 |
| Tensile Strength 3 (Break) | 124 | MPa | ASTM D638 |
| Tensile Stress (Break) | 121 | MPa | ISO 527-2/5 |
| Tensile Elongation 3 (Break) | 1.3 | % | ASTM D638 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 4 (50.0 mm Span) | 11600 | MPa | ASTM D790 |
| Flexural Modulus 5 | 11100 | MPa | ISO 178 |
| Flexural Strength | 180 | MPa | ISO 178 |
| Flexural Strength 4 (Break, 50.0 mm Span) | 178 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.44 | ||
| vs. Itself - Static | 0.35 |